Glass fiber cord with a hook weave ESS/HC Type

Technical specification – description

The cord ESS/HC type is manufactured from textured yarn made of boro-alumino-silicate E type glass of temperature resistance up to 650°C. Thanks to application of a knitting method of weaving, significant softness and flexibility of sealing have been achieved, which to a large extent facilitates fitting in fireplace inserts. A standard finished product is supplied on cardboard spools in sections of 100 running meters long.

Technical parameters:

PARAMETER DESCRIPTION VALUE
Type ESS/HC
Raw material Textured glass yarn type E Ø 9 µm
Method of execution Hooked, without core
Maximum temperature of short-term use 650º C
Maximum temperature of continuous use 500º C
Minimum temperature of use -100º C
pH range 3 - 14
Reinforcement type none
Density  0,6 g / cm3
Color Black or dark grey
Dimension range  Ø 5 – 14 mm


Glass fiber tapes

Technical specification – description

The glass fiber tape is manufactured from textured yarn made of boro-alumino-silicate E type glass of temperature resistance up to 650°C. Thanks to application of a knitting method of weaving, significant softness and flexibility of sealing have been achieved, which to a large extent facilitates fitting in fireplace inserts. A standard finished product is supplied on cardboard spools in sections of 100 running meters long.

PARAMETER DESCRIPTION VALUE
Type Free, without core
Raw material Glass yarn
Weave Plain, single-layer or multi-layer
(depending on thickness)
Maximum temperature of short-term use 650º C
Maximum temperature of continuous use 500º C
Minimum temperature of use -100º C
Melting point of fibers 1000º C
Contractility in % (24 h in 800° C)  Max. 3%
Density 1-1,1 g / cm3
Color Black or dark grey 
Dimension range  Width: 10 – 100 mm
Thickness: 2 – 20 mm